Nosso grupo organiza mais de 3.000 Séries de conferências Eventos todos os anos nos EUA, Europa e outros países. Ásia com o apoio de mais 1.000 Sociedades e publica mais de 700 Acesso aberto Periódicos que contém mais de 50.000 personalidades eminentes, cientistas de renome como membros do conselho editorial.

Periódicos de acesso aberto ganhando mais leitores e citações
700 periódicos e 15 milhões de leitores Cada periódico está obtendo mais de 25.000 leitores

Indexado em
  • Índice Copérnico
  • Google Scholar
  • Sherpa Romeu
  • Abra o portão J
  • Genâmica JournalSeek
  • Chaves Acadêmicas
  • PesquisaBíblia
  • Infraestrutura Nacional de Conhecimento da China (CNKI)
  • Acesso à Pesquisa Online Global em Agricultura (AGORA)
  • Biblioteca de Periódicos Eletrônicos
  • RefSeek
  • Universidade Hamdard
  • EBSCO AZ
  • OCLC – WorldCat
  • Catálogo online SWB
  • Biblioteca Virtual de Biologia (vifabio)
  • Publons
  • Fundação de Genebra para Educação e Pesquisa Médica
  • Euro Pub
  • ICMJE
Compartilhe esta página

Abstrato

Antibacterial ability of NiTi alloys by depositing Ag/collagen coatings

Shih-Fu Ou

NiTi alloys are one of the most important shape memory alloys because of their superior shape memory effect and peseudoelasticity compared to other shape memory alloys. NiTi alloys have been used in orthopaedic device applications, such as osteotomy fixation staples and intramedullary implants owing to their unique shape memory effect, superelasticity, low elastic modulus, and good resistance to fatigue. However, they suffer some drawbacks. The NiTi alloys lack antibacterial properties, and some patients are allergic to components with Ni. This study fabricated a Ag/collagen coating on a porous oxide film on NiTi alloy to improve the antibacterial ability of NiTi implants. Plasma electrolytic oxidation was first applied on NiTi to form a porous surface, which was then coated with silver through electrochemical deposition (ECP). Collagen was then used to modulate the amounts and shapes of the Ag during ECP. It was found that Ag aggregations with coarse dendritic structures were non-uniformly distributed on the surface. The distrubution of Ag aggregations was improved by deposition of collagen and Ag in the same time. The addition of collagen enables the silver aggregation to change to a sphere-like shape. Furthermore, the assistance of collagen also reduces the size of Ag aggregation. Cross-sectional TEM indicated that many Ag clusters are aggregated with each other and fill part of the pores on the oxide surface and inside the oxide film. The deposition of Ag on the oxide film causes the contact angle to increase, which suggests that the Ag-covered surface is hydrophobic. The Ag/collagen coating improves the hydrophilicity of the porous oxide film on NiTi alloy. The Ag/collagen coating can effectively prevent adhesion adn proliferation of Escherichia coli. The oxide film can protect the substrate from bacteria adhesion but cannot kill the bacterial in the suspension.